مشخصه یابی ریزساختاری آلیاژ Al-8Fe-1.4V-8Si تحت ریخته گری

Microstructural characterization of squeeze-cast Al–8Fe–1.4V–8Si

مشخصه یابی ریزساختاری آلیاژ  Al-8Fe-1.4V-8Si تحت فرایند ریخته گری فشاری

 

ABSTRACT

This paper investigates the effect of vanadium on the composition and morphology of intermetallics formed during the squeeze casting of Mgmodified Al–8Fe–1.4V–8Si alloy in both monolithic form and as-reinforced with 7.58, 10.52 and 15.68 wt.% SiC particles (SiCp). Iron intermetallics of -Al7(Fe,V)3Si and -Al18Fe11Si phases were predominantly observed in the alloy and composite. SEM studies and the EDX analyses revealed that refinement of Fe-intermetallics and modification of -phases to less deleterious morphologies of -phases has been achieved by vanadium addition of 1.4%. Also, heat treatment enhances V diffusion and SiC particles act as nucleation sites for the formation of finer -intermetallics. Fractographs exhibited cracking of long -phases and partial decohesion of SiCp from the matrix.

 مقاله انگلیسی (رایگان)

 چکیده

در این مقاله، اثر وانادیم بر ترکیب شیمیایی و ریزساختار ترکیبات بین فلزی تشکیل شده در حین فرایند ریخته گری فشاری در آلیاژ Al-8Fe-1.4V-8Si ، هم در حالت مونولیتی و هم بصورت تقویت شده با ذرات SiC (SiC_p) و با  درصدهای وزنی  58/7، 52/10 و 68/15، مورد بررسی قرار گرفته است. ترکیبات بین فلزی آهن شامل فازهای     α-Al₇(Fe,V)₃ و β-Al₁₈Fe₁₁Si بطور عمده در آلیاژ و کامپوزیت مشاهده شدند. بررسی های میکروسکوپ الکترونی روبشی (SEM) و آنالیز EDX نشان داد که ریزدانه شدن ترکیبات بین فلزی آهن و اصلاح فازهای β به ریزساختار مطلوب تر فازهای α توسط افزودن 4/1% وانادیم، بدست آمد. همچنین، عملیات حرارتی باعث افزایش نفوذ وانادیم گردید و ذرات SiC بعنوان مکان های جوانه زنی برای تشکیل ترکیبات بین فلزی α با ساختار     ریزدانه تر، عمل نمودند. بررسی سطح شکست نمونه ها ، ترک خوردن فازهای β و جدایش جزئی ذرات SiC_p از زمینه را، نشان داد.