سنتز دماپایین LaxBa1-x)B6) با تابع کار ترمویونی کوچک

Low temperature synthesis of low thermionic work function

LaxBa1x)B6)

سنتز دماپایین LaxBa1-x)B6) با تابع کار ترمویونی کوچک

ABSTRACT

This study presents investigations of the microstructure, morphology and emission properties of the promising thermionic material (LaxBa1−x)B6. The material was synthesised by solid-state reaction without post-synthesis purifications. Powder X-ray diffraction revealed that samples prepared at a temperature ⩾1500 °C had formed a significant proportion of solid solution (above 54 mass%). Subsequent sintering at 1950 °C caused the formation of a mixture of three solid solutions with the dominant phase being (La0.31Ba0.69)B6 ∼85% (by mass). The Richardson work function and emission constant for this boride mixture were found to be 1.03 eV and 8.44 × 10−6 A cm K−2 respectively.

   

   جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

این مطالعه، بررسی ریرساختار، مورفولوژی و خصوصیات نشری مواد ترمویونی با خصوصیات قابل اعتماد سیستم (LaxBa1-x)B6 را ارائه می‌دهد. این ماده توسط واکنش حالت جامد بدون تغلیض پس از سنتز، تولید شد. پراش اشعه‌ی X پودر نشان داد که نمونه‌های آماده شده در دمای C1500º≤ کسر بزرگی از محلول جامد (در حدود 54% جرمی) تشکیل داده‌اند. سینترینگ بعدی در دمای C1950º باعث تشکیل مخلوطی از سه محلول جامد با فاز غالب (La0.31Ba0.69)B6 به میزان 85% جرمی می‌شود. تابع کار ریچاردسون  و ثابت نشر برای این مخلوط بوریدی به‌ترتیب با مقدار eV 1.03 و AcmK-2 10-6×8.44 ارزیابی شده است.