Synthesis of hydroxyapatite via mechanochemical treatment

سنتز هیدروکسی آپاتیت با استفاده از عملیات مکانوشیمیایی

ABSTRACT

Hydroxyapatite powder was synthesized with calcium pyrophosphate (Ca2P2O7) and calcium carbonate (CaCO3) through solid-state reaction. The two powders were mixed in acetone and water, respectively, and the single phase of hydroxyapatite was observed to occur only in the powder milled in water, without the additional supply of water vapor during heat-treatment at 1100°C for 1 h. The results were explained in terms of the mechanochemical reaction that could supply enough amount of hydroxyl group to the starting powders to form a single phase of hydroxyapatite. Practical implication of the results is that the powder of high crystalline hydroxyapatite can be obtained by the simple milling in water and subsequent heat-treatment.

 

  جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

پودر هیدروکسی آپاتیت با کلسیم پیروفسفات (Ca2P2O7) و کربنات کلسیم (CaCO3) از طریق واکنش حالت جامد سنتز شد. هر دو پودر به ترتیب در استون و آب مخلوط شده و. هیدروکسی آپاتیت تک فاز، بدون تأمین بخار آب اضافی در طول عملیات حرارتی یک ساعته در C°1100، تنها در پودری که در آب آسیاب شد، بدست آمد. نتایج با واکنش مکانوشیمیایی تفسیر شد که توانست جهت تشکیل هیدروکسی آپاتیت تک فاز، مقدار کافی گروه های هیدروکسیل را برای پودرهای پیش ماده اولیه تأمین کند. از روی نتایج می توان استنباط کرد که پودر هیدروکسی آپاتیت با میزان بلورینه شدن بالا، با آسیاب ساده در حضور آب و عملیات حرارتی متعاقب آن، قابل دستیابی است.