خواص مواد نانوساختار مس- WC

Characterisation of nanostructured copper - WC materials

خواص مواد نانوساختار مس- WC

ABSTRACT

Purpose: The aim of this work was to determine the microstructure and properties stability of nanocrystalline copper dispersion hardened with nanoparticles of tungsten carbides.

Design/methodology/approach: Tests were made with Cu and Cu – WC micro – composites containing up to 3% of a hardening phase. The materials were fabricated by powder metallurgy techniques, including milling of powders, followed by their compacting and sintering. The main mechanical properties of the materials were determined from the compression test, and, moreover, measurements of the HV hardness and electrical conductivity have been made. Analysis of the initial nanocrystalline structure of these materials was made and its evolution during sintering was investigated.

   

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

هدف: هدف این پژوهش بررسی ریزساختار و پایداری خواص نانوبلور مس سخت شده (سخت شده توزیعی) با نانوذارت تنگستن کارباید است.

طراحی/ روش شناسی/ روش: آزمون ها با Cu و میکروکامپوزیت های Cu-WC محتوی تا 3 درصد فاز سخت کننده، انجام شدند. مواد با روش های متالورژی پودر، شامل آسیاب پودرها و سپس فشردگی و سینتر کردن آنها، ساخته شدند. خواص مکانیکی اصلی مواد از آزمون های فشار و علاوه بر این اندازه گیری سختی HV (ویکرز) و رسانایی الکتریکی بدست آمد. آنالیز ساختار نانوبلورین اولیه این مواد انجام شده و سیر تحولات آن در طول سینترشدن، مورد بررسی قرار گرفت.