اثر ریزساختار بر رفتار سایشی گلوله‌های آسیاب از جنس چدن پرکروم

Effect of microstructure on wear behavior of

high Chromium cast iron milling balls

اثر ریزساختار بر رفتار سایشی گلوله‌های آسیاب از جنس چدن پرکروم

ABSTRACT

In milling and grinding of minerals, balls which can be made of high chromium white cast iron are loaded into the milling container. Under the operating conditions of milling, the balls are subjected to impact, rolling, fatigue and corrosion wears which cause fracture and deforming the balls [1,2]. Since the wear conditions are unchangeable and inevitable, control of the ball dimensions, ball material, alloying and heat treatment must meet the required conditions to provide good wear and erosion resistance [3,4]. Generally, the balls are chosen from high chromium cast iron to provide hard carbide within the martensitic matrix with a little retained austenite to result in the best wear resistance for the operating conditions of the balls [5].

  

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

در آسیاکاری و خردایش مواد معدنی، گلوله‌ها که می‌توانند از جنس چدن سفید پرکروم باشد، به همراه ماده‌ی معدنی به داخل محفظه شارژ می‌شوند. در شرایط کاری آسیا، گلوله‌ها هم در معرض سایش‌های ضربه‌ای، غلتشی، خستگی و خوردگی قرار دارند که موجب شکست و تغییر شکل آنها می‌شود[1،‌ 2]. از آنجایی که شرایط سایش قابل تغییر نیست و این شرایط اجتناب ناپذیر است، بنابراین کنترل ابعاد گلوله، جنس گلوله، آلیاژسازی و عملیات حرارتی آن باید به گونه‌ای باشد که مقاومت به سایش و فرسایش خوبی به وجود آید[4,3]. معمولا گلوله‌ها از جنس چدن پرکروم انتخاب می‌شوند که وجود کاربید سخت در زمینه مارتنزیتی با مقدار کمی آستنیت باقیمانده می‌تواند بهترین مقاومت به سایش را برای شرایط کاری این نوع گلوله‌ها مهیا کند[5].