چاپ سه بعدی کامپوزیت کربن/کربن توسط زینتر لیزر انتخابی

Three dimensional printing of carbon/carbon composites

by selective laser sintering

چاپ سه بعدی کامپوزیت کربن/کربن توسط زینتر لیزر انتخابی

ABSTRACT

A novel three dimensional (3D) printing method is developed to fabricate complex carbon/carbon (C/C) composite components. The C/C composites with the high mechanical performance are achieved by combining the selective laser sintering and the chemical vapor infiltration-thermal treatment process. The C/C composites with a maximum density of 1.5 g/cm3 and bending strength of 100 MPa are obtained. Complex C/C composite parts with the minimum thickness of 0.5 mm are accurately fabricated with the computer-aided design technique. This developed 3D printing method can be well applied to the production of complex C/C composite parts with high precision and good mechanical performance.

   

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

روش چاپ سه بعدی جدید به منظور ساخت ترکیب های کامپوزیتی کربن/کربن پیچیده ایجاد شده است. کامپوزیت های کربن-کربن با عملکرد بالا توسط ترکیب زینتر لیزر انتخابی و فرایند عملیات حرارتی- نفوذ بخار شیمیایی بدست آمده است. کامپوزیت های کربن-کربن با بیشترین دانسیته حدود 1.5گرم/سانتی متر مکعب و استحکام خمشی 100مگاپاسکال بوجود آمده اند. اجزای کامپوزیت کربن /کربن پیچیده با حداقل ضخامت  0.5میلی متر  با دقت به روش طراحی به کمک کامپیوتر ساخته شده است. از روش چاپگر سه بعدی ایجاد شده می توان برای تولید اجزای کامپوزیت های کربن-کربن پیچیده با دقت بالا و عملکرد مکانیکی خوب استفاده کرد.