سنتز شیمیایی لایه های نازک نانوکریستال کادمیوم تلوریم

Structural and optical properties of CdTe-nanocrystals

thin films grown by chemical synthesis

خواص نوری و ساختار لایه های نازک نانوکریستال CdTe رشد کرده به روش سنتز شیمیایی

ABSTRACT

By mans of a chemical synthesis technique stoichiometric CdTe-nanocrystals thin films were prepared on glass substrates at 70 °C. First, Cd(OH)2 films were deposited on glass substrates, then these films were immersed in a growing solution prepared by dissolution of Te in hydroxymethane sulfinic acid to obtain CdTe. The structural analysis indicates that CdTe thin films have a zinc-blende structure. The average nanocrystal size was 19.4 nm and the thickness of the films 170 nm. The Raman characterization shows the presence of the longitudinal optical mode and their second order mode, which indicates a good crystalline quality. The optical transmittance was less than 5% in the visible region (400–700 nm). The compositional characterization indicates that CdTe films grew with Te excess.

   

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

لایه های نازک نانوکریستال CdTe استوکیومتری، به روش سنتز شیمیایی ابتدا روی یک زیرلایه شیشه ای در دمای C°70 آماده شدند، لایه های Cd(OH)2 روی زیرلایه شیشه ای رسوب نشانی گشتند، سپس این لایه ها در یک محلول رشد داده شده به وسیله انحلال Te در اسید سولفینیک هیدروکسی متان غوطه ور شدند تا CdTe بدست آید. آنالیز ساختاری نشان می دهد که لایه های نازک CdTe ساختار بلند روی دارند. میانگین اندازه ذرات نانوکریستال nm 4/19 و ضخامت لایه ها nm 170 بود. طیف Raman حضور مُد اپتیکی طولی و مُد دوم را نشان می دهد که از کیفیت مناسب کریستالی حکایت دارد. عبوردهی نور در ناحیه مرئی (nm 700- 400) کمتر از 5% بود. آنالیز ترکیب هم نشان داد که لایه های CdTe با Te اضافی رشد کرده اند.