اثر عملیات حرارتی بر ریزساختار و خواص مکانیکی فولاد زنگ‌نزن دوپلکس

Effect of heat treatment on microstructure and

mechanical properties of duplex stainless steel

اثر عملیات حرارتی بر ریزساختار و خواص مکانیکی فولاد زنگ‌نزن دوپلکس

ABSTRACT

Present study concerns the effect of deformation and heat treatment on the microstructure and mechanical properties of a duplex stainless steel. While hot rolling causes the coarse distribution of the constituent phases (ferrite and austenite), 50% cold rolling results into the elongated and splintered two — phase structure. Supersaturated ferrite structure established by water quenching from 1300°C results into the strengthening due to the formation of fine dispersed austenite precipitates within ferrite grain after isothermal heat treatment (1000°C, 0.5 hour). Duplex structure consisting of ferrite and austenite in a fine-grained form is obtained after isothermal heat treatment of cold rolled sample. Cold deformed and heat treated steel exhibits best combination of strength and ductility among all the investigated steel samples.

   

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

تحقیق حاضر به اثر تغییرشکل و عملیات حرارتی بر ریزساختار و خواص مکانیکی فولاد زنگ‌نزن دوپلکس می‌پردازد. درحالی که نورد گرم باعث توزیع درشت فازهای سازنده (فریت و آستینیت) می‌شود، 50% نورد سرد منجر به ساختار کشیده و خردشده‌ی دوفازی می‌گردد. ساختار فریت فوق‌اشباع که توسط کوئنچ از 1300°C در آب ساخته شده بود منجر به استحکام‌بخشی ناشی از تشکیل رسوبات آستنیتی دارای توزیع ظریف درون دانه‌ی فریت پس از عملیات حرارتی همدما (1000°C، 0.5 ساعت) می‌شود. ساختار دوپلکس متشکل از فریت و آستنیت در حالت ریزدانه پس از عملیات حرارتی همدمای نمونه‌ی نورد سرد شده بدست می‌آید. فولاد تغییرشکل سرد یافته و عملیات حرارتی شده بهترین ترکیب از استحکام و داکتیلیتی را در میان نمونه‌های فولادی بررسی شده نشان می‌دهد.