پیشرفت‌ها در فناوری پالایش فولاد و چشم‌انداز آینده

Advances in Steel Refining Technology and Future Prospects

پیشرفت‌ها در فناوری پالایش فولاد و چشم‌انداز آینده

ABSTRACT

By the 1980s, Nippon Steel Corporation established a separated refining process based on hot-metal pretreatment,2) whereby the contents of silicon, sulfur, and phosphorus in hot metal were decreased before the decarburization in converters, using torpedo ladle cars, hot-metal ladles, or converters as the reaction vessels. Thereafter, technical developments such as the following were achieved:
separation of desulfurization from the other hot-metal pretreatment; separate processing of hot-metal dephosphorization from decarburization; development of hot-metal dephosphorization using converters as the reaction vessels and not requiring fluorine; improvement in reaction efficiency of these processes; recycled use of slag; adjustment of silicon content in hot metal in case of excessively high Si; and increase in converter capacity for hot-metal dephosphorization in converters.

 

 

چکیده

با فرارسیدن دهه‌ی 1980، شرکت فولاد نیپون یک فرآیند پالایش جداسازی‌شده برمبنای پیش‌عملیات روی فلز داغ پایه‌گذاری کرد2، که در آن پیش از کربن‌زدایی در مبدل (کنورتور)، با استفاده از پاتیل‌های اژدر واگنی ، پاتیل‌های فلز داغ یا مبدل‌‌هایی که به عنوان محفظه واکنش بودند، مقادیر سیلیسیوم، گوگرد و فسفر در فلز داغ کاهش پیدا می‌کردند. پس از آن، پیشرفت‌های فنی شامل موارد پیش‌رو بدست آمدند:

جداسازی گوگردزدایی از پیش‌عملیات دیگر روی فلز داغ؛ فرآوری فسفرزدایی فلز داغ بطور جداگانه‌ نسبت به کربن‌زدایی؛ توسعه فسفرزدایی فلز داغ با استفاده از مبدل‌ها به عنوان محفظه‌ واکنش بدون نیاز به فلوئور؛ بهبود راندمان این فرآیندها؛ استفاده از سرباره‌ی بازیافت‌شده؛ تنظیم میزان سیلیسیوم در فلز داغ در مقادیر بسیار زیاد Si؛ و افزایش ظرفیت تبدیل در مبدل‌ها برای فسفرزدایی از فلز داغ.