پیوند نفوذی فاز مایع گذرا با استفاده از پوشش‎های نانوپراکنده‎ی Ni

Transient liquid phase diffusion bonding Al-6061 using

nano-dispersed Ni coatings

پیوند نفوذی فاز مایع گذرا با استفاده از پوشش‎های نانوپراکنده‎ی Ni

ABSTRACT

Transient liquid phase diffusion bonding (TLPDB) of Al-6061 containing 15 vol.% alumina particles was carried out at various bonding temperatures. A 5 μm thick electrodeposited Ni-coating containing 18 vol.% nano-size alumina particles was used at the interlayer. Joint formation was attributed to the solid-state diffusion of Ni into the Al-6061 alloy followed by eutectic formation and isothermal solidification at the joint interface. Examination of the joint region using scanning electron microscopy (SEM), wavelength dispersive spectroscopy (WDS) and X-ray diffraction (XRD) showed the formation of intermetallic phases such as Al3Ni, Al9FeNi and Ni3Si within the joint zone. The results indicate that the incorporation of nano-size Al2O3 dispersions into the interlayer can be used to improve joint strength.

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

  

چکیده

پیوند نفوذی فاز مایع گذرای(TLPDB) آلیاژ Al-6061 شامل ذرات آلومینای 15% حجمی در دماهای مختلف پیوند به انجام رسید. پوشش Ni آبکاری شده با ضخامت 5میکرومتر شامل نانوذرات آلومینای 18% حجمی در میان‎لایه‎ مورد استفاده قرار گرفت. تشکیل محل اتصال به نفوذ در حالت جامد Ni در آلیاژ Al-6061 مطابق با تشکیل یوتکتیک و انجماد همدما در سطح مشترک محل اتصال نسبت داده شد. آزمایش ناحیه‎ی اتصال با استفاده از میکروسکوپ الکترونی روبشی(SEM)، میکروسکوپ پراکندگی طول موج(WDS) و پراش اشعه‎ی ایکس(XRD)، تشکیل فازهای بین‎فلزی را مانند Al3Ni، Al9FeNi و Ni3Si در ناحیه‎ی اتصال نشان داد. نتایج نشان داد که اتصال پراکندگی‎های نانوذرات Al2O3 در میان‎لایه می‎تواند به منظور تقویت استحکام محل اتصال مورد استفاده قرار بگیرد.