خواص سایش پوشش CrC–37WC–18M رسوب داده شده

Wear properties of CrC–37WC–18M coatings deposited by

HVOF and HVAF spraying processes

خواص سایش پوشش CrC–37WC–18M رسوب داده شده

توسط فرایندهای پاشش HVOF و HVAF

 

ABSTRACT

CrC–37WC–18M cermet coatings were deposited using new feedstock powders which seem to combine the properties of WC–CoCr and CrC–NiCr coatings. A conventional particle size CrC–37WC–18M powder was used as feedstock for the HVOF (high velocity oxygen fuel) thermal spraying process and a fine particle distribution was used as feedstock for the HVAF (high velocity air fuel) thermal spraying process. In order to characterize the morphology of the feedstock powders and deposited coatings SEM and X-ray diffraction were used. The microhardness of the coatings was also studied. The wear behavior of the coatings was evaluated by pin-on-disk and rubber wheel abrasion tests. The HVAF coating showed equal or even better wear resistance as compared to corresponding HVOF coatings

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

 

 

چکیده

پوشش های سیمانی CrC–37WC–18M با استفاده از پودرهای مواد اولیه جدید رسوب گذاری شده اند که به نظر می رسد خواص پوشش های WC-CoCr و CRC-NiCr را ترکیب کند. اندازه متداول ذرات پودر CRC-37WC-18M به عنوان مواد اولیه برای فرآیند پاشش حرارتی HVOF (سرعت بالای سوخت اکسیژن) و ذرات با توزیع ریز به عنوان مواد اولیه برای فرآیند پاشش حرارتی HVAF (سرعت بالای سوخت هوا) استفاده شدند. به منظور مشخصه یابی مورفولوژی پودر مواد اولیه و پوشش های رسوب داده شده،  SEM و پراش اشعه ایکس مورد استفاده قرار گرفتند. میکروسختی پوشش نیز مورد مطالعه قرار گرفت. رفتار سایش پوشش ها توسط آزمون های پین روی دیسک و سایش چرخ لاستیکی بررسی گردید. پوشش HVAF مقاومت سایش برابر یا حتی بیشتری در مقایسه با پوشش های HVOF متناظر نشان داد.