وضعیت صنعت در کنترل آخال ها در طی ریخته گری شمش فولادی

State of the Art in the Control of Inclusions during Steel
Ingot Casting

وضعیت صنعت در کنترل آخال ها در طی ریخته گری شمش فولادی

ABSTRACT

This article extensively reviews published research on inclusions in ingot steel and defects on ingot products, methods to measure and detect inclusions in steel, the causes of exogenous inclusions, and the transport and entrapment of inclusions during fluid flow, segregation, and solidification of steel cast in ingot molds. Exogenous inclusions in ingots originate mainly from reoxidation of the molten steel, slag entrapment, and lining erosion, which are detailed in this article. The measures to prevent the formation of exogenous inclusions and improve their removal are provided, which are very useful for the clean steel production of ingot industries.

   مقاله انگلیسی (رایگان)

  چکیده

این مقاله به طور وسیعی پژوهش منتشر شده درباره آخال ها در شمش فولاد و عیوب روی شمش تولیدی، روش های اندازه گیری و یافتن آخال ها در فولاد را مرور می کند، که از آخال های بیرونی، و انتقال و به دام افتادن آخال ها در طی جریان سیال، جدایش، و انجماد قطعه ریختگی فولادی در قالب های شمش ناشی می شود. آخال های بیرونی در شمش ها اساساً از اکسیداسیون مجدد فولاد مذاب، به دام انداختن سرباره، و فرسایش خطی ناشی می شود، به طوری که در این مقاله شرح داده می شود. پیش بینی هایی برای جلوگیری از تولید آخال های بیرونی و بهتر شدن تفکیک آن ها فراهم شد، به طوری که برای تولید فولاد خالص از شمش صنعتی بسیار مفید است.