سنتز، شناسایی و خواص نوری نانوذرات اکسید روی

Synthesis, characterization and optical properties of zinc oxide nanoparticles

سنتز، شناسایی و خواص نوری نانوذرات اکسید روی

ABSTRACT

Zinc oxide nanoparticles were synthesized using a simple precipitation method with zinc sulfate and sodium hydroxide as starting materials. The synthesized sample was calcined at different temperatures for 2 h. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and proton-induced X-ray emission (PIXE) analysis. SEM images show various morphological changes of ZnO obtained by the above method. The average crystallite sizes of the samples were calculated from the full width at half maximum of XRD peaks by using Debye-Scherrer's formula and were found to be in the nanorange. EDS shows that the above route produced highly pure ZnO nanostructures. PIXE technique was used for trace elemental analysis of ZnO. The optical band gaps of various ZnO powders were calculated from UV-visible diffuse reflectance spectroscopic studies.

  جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

 چکیده

نانوذرات اکسید روی با استفاده از یک روش ته نشینی ساده با سولفات روی و هیدروکسید سدیم به عنوان مواد آغازین سنتز شد. نمونه سنتز شده در دماهای مختلف برای 2 ساعت کلسینه شد. نمونه ها توسط آنالیزهای پراش اشعه X (XRD) ، میکروسکوپ الکترونی روبشی (SEM)، طیف سنجی پراش انرژی پرتو ایکس (EDS) ، و آنالیز گسیل پرتوی ایکس با تابش پروتون (PIXE) شناسایی شدند . تصاویر SEM تغییرات مورفولوژیکی ZnO بدست آمده از روش فوق را نشان داد. اندازه های کریستالی متوسط نمونه ها از عرض کامل در نصف بیشترین پیک XRD با استفاده از فرمول دبای-شرر محاسبه شد و در محدوده نانو نشان داده شد. EDS نشان داد که در مسیر فوق نانوساختارهای ZnO با خلوص بالایی تولید شد. تکنیک PIXE برای پی بردن به آنالیز عنصری ZnO استفاده شد. باندهای گپ نوری پودرهای ZnO متنوع از بررسی های طیف سنجی بازتاب پخشی مرئی-فرابنفش UV بدست آمد.